Introduction
| Properties | Test Method | Requirements | Results | Verdicts | |
| Water absorption | EN ISO 10545-3:2018 |
Eb≤0.5% | 0.08% | P | |
| Percent mass fraction | Individual maximum 0.6% | 0.07%~0.09% | P | ||
| Breaking strength, in N | EN ISO 10545-4:2019 |
≥1300 | 4717 | P | |
| Modulus of rupture, in Mpa | EN ISO 10545-4:2019 |
Minimum≥35 | - | N/A | |
| Not applicable to tiles with breaking strength≥3000N | Individual minimum≥32 | - | N/A | ||
| Abrasion resistance | EN ISO 10545-7:1998 |
Report abrasion class | Class 4 | - | |
| Resistance to surface abrasion of glazed tiles intended for use on floors | Report cycles passed | 2100 | - | ||
| Coefficient of linear thermal expansion:from ambient temperature to 100°C | EN ISO 10545-8:2014 |
Declared value | 6.0X 10-6°C-1 | - | |
| Thermal shock resistance | EN ISO 10545-9:2013 |
Pass | Fully resistance | P | |
| Crazing resistance: glazed tiles | EN ISO 10545-11:1996 |
Pass | Fully resistance | P | |
| Frost resistance | EN ISO 10545-12:1997 |
Pass | Fully resistance | P | |
| Impact resistance: Coefficient of restitution (COR) | EN ISO 10545- 5:1997 |
Declared value | 0.87 | - | |
| Slipperiness | Shod Ramp Test, critical angle, ages | DIN 51130:2014 | Declared value | Dr :55 | |
| Pendulum friction test , PTV 96 | CEN/TS 16165:2016 |
Wet:15 | |||
| Reaction to fire | CWT | ClassA1 or A1FL A1 or A1FL |
Used for walls: Class A1 Used for floorings: Class A1fl |
P | |
| Resistance to staining | EN ISO 10545-14:2015 |
Minimum Class 3 | Class5 | P | |